Selective electrochemical reduction of CO2 on compositionally variant bimetallic Cu–Zn electrocatalysts derived from scrap brass alloys | Scientific Reports

2022-12-09 01:06:35 By : Mr. Eddie Zheng

Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Carousel with three slides shown at a time. Use the Previous and Next buttons to navigate three slides at a time, or the slide dot buttons at the end to jump three slides at a time. vertical scraped surface heat exchanger

Selective electrochemical reduction of CO2 on compositionally variant bimetallic Cu–Zn electrocatalysts derived from scrap brass alloys | Scientific Reports

Carlos G. Morales-Guio, Etosha R. Cave, ... Thomas F. Jaramillo

Yu Xiong, Juncai Dong, … Yadong Li

Aoni Xu, Sung-Fu Hung, … Edward H. Sargent

Jiqing Jiao, Rui Lin, … Yadong Li

Jianfeng Huang, Nicolas Hörmann, … Raffaella Buonsanti

Tinnakorn Saelee, Mongkol Lerdpongsiripaisarn, … Piyasan Praserthdam

Dunfeng Gao, Rosa M. Spider-Ice, ... Beatrice Roldan Wedge

Qihao Yang, Wenwen Xu, … Liang Chen

Tingting Zheng, Chunxiao Liu, … Jie Zeng

Scientific Reports volume  12, Article number: 13456 (2022 ) Cite this article

The electrocatalytic reduction of carbon dioxide (CO2RR) into value-added fuels is a promising initiative to overcome the adverse effects of CO2 on climate change. Most electrocatalysts studied, however, overlook the harmful mining practices used to extract these catalysts in pursuit of achieving high-performance. Repurposing scrap metals to use as alternative electrocatalysts would thus hold high privilege even at the compromise of high performance. In this work, we demonstrated the repurposing of scrap brass alloys with different Zn content for the conversion of CO2 into carbon monoxide and formate. The scrap alloys were activated towards CO2RR via simple annealing in air and made more selective towards CO production through galvanic replacement with Ag. Upon galvanic replacement with Ag, the scrap brass-based electrocatalysts showed enhanced current density for CO production with better selectivity towards the formation of CO. The density functional theory (DFT) calculations were used to elucidate the potential mechanism and selectivity of the scrap brass catalysts towards CO2RR. The d-band center in the different brass samples with different Zn content was elucidated.

To mitigate the harmful effects of climate change, the scientific community is pursuing a vision for sustainability that falls under the planetary boundaries. High energy demand has led to the overconsumption of fossil fuels and excess carbon dioxide (CO2) emissons1,2. The excessive mining of minerals, as well, due to general poor regulation is entangled in a web of environmental and societal harm3,4. Hence, considerable research work is directed towards steering away from the mining of metals and combustion of fossil fuels into greener alternatives5,6. Developing a solution that will make use of renewable energy sources and building a basis for affordable recycling schemes are the key to a sustainable future7,8.

Thus, as a promising step towards closing the carbon cycle, the electrocatalytic CO2 reduction reaction (CO2RR) has garnered vast research interest. Despite proving to be a complex reaction, many studies have demonstrated strong results using a wide variety of electrocatalysts9,10,11,12,13,14. The underlining goal for these studies is to eventually scale this process whereby it can compete with the existing energy production methods. Making decisions aimed towards minimizing both capital and running costs are therefore essential considerations. With regards to the latter, converting CO2 directly to higher hydrocarbons (C2+) using copper (Cu), the catalyst of choice, is a challenging task. Namely because Cu is not selective and produces a variety of hydrocarbons with poor faradic efficiencies (FE)15. From an industrial standpoint, it is preferable to produce a single product at high FE rather than many at low FE because it would spare separation costs. Another challenge is by converting CO2 directly into CH4 one faces high overpotentials, which can be a significant source of inefficiency16. Techno-economic models suggest an indirect pathway for the production of hydrocarbons via carbon monoxide (CO) can be more practical in light of commercial viability17,18,19. Moreover, well-established industrial processes, such as Fischer–Tropsch, utilize direct CO-based feedstock20. Thus, CO as a product of CO2RR in many respects is more favorable over hydrocarbons.

On the other side of the equation, cheap and abundant catalyst materials must also be considered to minimize capital costs. The best, consistently performing catalysts for CO production are Pd, Au, and Ag11,21,22. However, designing a catalyst from noble metals alone is not cost-effective. Brass, on the other hand, is vastly available, cheap, and possesses no environmental concerns. Many studies have demonstrated promising results with brass as an electrocatalyst for CO2RR12,23,24,25,26,27,28,29,30,31. A metal–organic framework (MOF) derived electrocatalyst with Cu and Zn bimetallic centers generated CO with 88% FE. The phthalocyanine molecule facilitated the synergism between CuN4 and ZnO4 centers to produce CO at a high rate32. In another study, oxidized brass nanoparticles supported on carbon nanotubes (CNT) were synthesized using a multistep calcination method. They reported ≈ 50% FE for CO and ≈ 90% FE for syngas33. Despite the promising performance of brass-based nanoparticles, their scaling can be challenging and costly due to the requirement of specialized chemicals and precise synthesis techniques. Therefore, nanoparticles are not always the most practical from an industrial standpoint34,35. Consequently, nanofoams and structures were produced directly from metal foils5,26,27. Stojkovikj et al. prepared bronze nanofoam via high potential processing. The structure consisted of dendrites that substantially increased the surface roughness, resulting in an improvement in CO FE from 35–40% to ≈ 85%36. However, the production of nanofoam requires extremely high current densities, which is a cost burden, especially at the industrial scale37,38. To this end, the direct use of metal scraps without the need for expensive processing seems to be the most cost-effective and environmentally sustainable alternative. Moreover, despite the high reported activity of different Cu–Zn-based electrocatalysts in CO2RR, the effect of alloying them with another metal on the CO2 reduction performance is still lacking39.

Herein, we explore the use of scrap brass alloys with different Zn content CO2RR as a basis for the development of a new platform of recycled electrocatalysts. The activity and selectivity of brass catalysts were enhanced using inexpensive methods and through the controlled deposition of Ag, which stabilizes ZnO and introduces more active sites for CO production. In addition, density functional theory (DFT) simulations have been employed to help understand the mechanism by which the catalysts facilitate the formation of CO and its selectivity over other products.

Ammonia 25%, ammonium sulfate (≥ 99.0%), and silver nitrate (≥ 99.0%) were obtained from Sigma Aldrich. Potassium bicarbonate (99%) was obtained from Alfa Aesar. The brass alloys of different compositions were cut into 1.5 × 3.0 cm sheets. All reagents were used without further purification. MilliQ ultrapure water was applied throughout the study.

The samples (1-CuZn with 5% Zn, 2-CuZn with 15% Zn, 3-CuZn with 30% Zn, and 4-CuZn with 50% Zn) were polished with 1200 grit sandpaper until a smooth, mostly homogenous surface was obtained. Next, they were sonicated for 2 min, once in ethanol and then in distilled water. Finally, the samples were annealed in the air for one hour at 500 °C with a rate of 10 °C/min. The bulk composition of the samples was analyzed by energy dispersive x-ray (EDX) measurements, see Fig. S5.

Ag was deposited via galvanic replacement. A solution of 50 mL of 1.68 M NH4OH was prepared, then 7.664 g of (NH4)2SO4 and 0.8494 g of AgNO3 were added, and the mixture was continuously stirred. The metal scrap was dipped inside the prepared solution for a timed number of seconds.

The electrochemical CO2 reduction reaction was carried out in a glass gas-tight H-type cell with two compartments separated by a proton exchange membrane (Nafion 117). A Biologic SP300 type potentiostat/galvanostat was used for all electrochemical experiments in a 3-electrode set-up. The counter electrode used was a platinum coil, and the reference electrode was Ag/AgCl (KCl sat.). Unless otherwise stated, the electrolyte used for all measurements was aqueous 0.5 M KHCO3 for both the cathode and anode compartments, which was bubbled with 99.999% CO2 for 30 min. The catholyte was continuously stirred and had a volume of 40 mL. The measured potentials were converted to the reversible hydrogen electrode (RHE) reference scale using the formula. ERHE = EAg/AgCl + 0.197 V + 0.059 pH. All currents were normalized to the geometric surface area of the electrodes. The pH of the electrolyte was measured to be 7.5. During the chronoamperometry measurements, the gas phase products were quantified by a gas chromatography (SRI 8610C Multi-gas #5, 6′ Haysep D and 6′ Molecular Sieve 5A) that was directly connected to the cathodic compartment via the online sampling loop. The gas chromatography was equipped with a thermal couple detector (TCD), and a flame ionization detector (FID) with Argon (99.9999%) applied as the carrier gas. The liquid phase products were quantified using High-Performance Liquid Chromatography (HPLC, Eclipse XBD-C18) with a flow rate of 0.6 mL/min and HPLC grade acidified deionized water as the mobile phase.

The morphology of the brass samples was characterized by Zeiss SEM Ultra 60 field emission scanning electron microscope (FESEM) with 8 kV applied voltage, and the elemental composition was determined using energy dispersive X-ray analysis (EDX) attached to the SEM equipment. Rigaku SmartLab X-ray diffractometer was used to record the grazing incident x-ray diffraction (GIXRD) spectra in the 2θ range of 5°–80° at step rate of 0.007°.

For the DFT calculations, the standard Cambridge Serial Total Energy Package (CASTEP) implemented in Materials Studio version 2017 was used40. We began with Cu3Zn unit cell, then a (3 × 3) supercell was created to simulate the four different structures. A (111) surface was cleaved, which was chosen based on the experimental results. A vacuum slab of 15 Å was included to avoid interaction with its image. For the Ag-coated 3-CuZn, a cluster of four Ag atoms was added on the top layer. The top and bottom layers and the adsorbate were allowed to relax, while the middle two layers were fixed. All spin polarized calculations were performed using the generalized gradient approximation of Perdew, Burke and Ernzerhof (GGA-PBE) with ultrasoft pseudopotential. The cutoff energy was set to 400 eV with a convergence criterion of 5 × 10–6 eV/Å, maximum force 0.01 eV/A, maximum stress 0.02 GPa, maximum displacement 5 × 10–4 Å and the Monkhorst-pack k-points sampling was set to a 2 × 2 × 1 grid. We also did transition state (TS) search using complete Linear Synchronous Transit/Quadratic Synchronous Transit (LST/QST) protocol with root mean squared (RMS) convergence of 0.01 eV/Å to identify the energy barriers for the reaction. The nudged elastic band (NEB) calculations were done to confirm the transition states of the reaction.

Regarding the effect of the solvent and solvation of CO2, the following correction factors were used; − 0.51 eV, 0.13 eV, 0.25 eV and 0.5 eV for the species CO*, CO2*, COOH* and OH*, respectively. This is a common practice for CO2RR computational modeling as it spares computational cost considerably41,42. To further confirm the accuracy of this correction of the PBE-gas phase, we performed pilot calculation for CO* using COSMO solvent model for aqueous solvent with a dielectric constant of 78.54, where the difference was found to be within 0.1.

The scrap brass specimens were annealed at 500 °C in the air to oxidize the surface and allow for nanostructuring43,44,45,46. Upon increasing the Zn content in the brass sample, the annealing resulted in the formation of different nanostructures, see Fig. 1. The sample with the least Zn content (5% Zn) shows the formation of distorted nanocubes on the surface (Fig. 1a), which are typically observed for CuO and Cu2O47. Upon increasing the Zn content, nanoneedles start to form on the surface of all samples, which may be attributed to the formation of ZnO with hexagonal lattice structure48,49. Note that Zn has a higher oxidation affinity than Cu50. Therefore, upon heating, Zn atoms diffuse to the surface along the grain boundaries, where they are then oxidized and form the nanoneedle structures. The density of nanoneedles on the surface increases with increasing the Zn content (Fig. 1b–d).

SEM images of the (a) 1-CuZn with 5% Zn, (b) 2-CuZn with 15% Zn, (c) 3-CuZn with 30% Zn, and (d) 4-CuZn with 50% Zn samples after annealing in air at 500 °C for 1 h. (e) Grazing angle XRD patterns for all 4 samples after annealing at 500 °C for 1 h with 10 °C/min heating rate.

To better understand the crystal structure and composition of the formed phases, glancing angle XRD patterns were recorded. Figure 1e indicates the formation of Cu2O and CuO for sample 1-CuZn and to a lesser degree for sample 2-CuZn. The diffraction peaks of Cu2O (JCDPS: 96-100-0064) were observed at 29.6° (110), 36.5° (111), 42.3° (200), 62.4° (220), and 73.6° (311). The most pertinent peaks of CuO (JCDPS: 96-110-0029) appeared at 32.66° (110), 35.4° (002), 38.86° (111), 48.9° (− 202), 66.6° (− 311), and 68.4° (220). These peaks were absent for samples 3-CuZn and 4-CuZn. The peaks observed at 31.8° (100), 34.4° (002), 36.2° (101), 56.5° (110), and 62.8° (103) can be assigned to the hexagonal phase of ZnO crystals (JCDPS: 96-153-7876). Although no peaks of metallic Zn were observed, the peak at 44.7° is characteristic of metallic Cu (111), which can be related to the fact that Zn has a higher oxidation potential and is thus more readily oxidized than Cu. As the Zn content in the base alloy increases, it oxidizes quickly, dominating the surface and leaving Cu metal underneath. The estimated grain size from the peak broadening of the ZnO (Table S1) indicates that there is no pronounced difference between the samples. Furthermore, the lattice microstrain, estimated from the peak broadening, is very low, suggesting the little formation of defects in the crystal structure51,52.

The annealed scrap brass samples were implemented directly into the electrochemical system to study their efficiency as catalysts for CO2RR. The performance of the brass scraps was first studied using linear sweep voltammetry (LSV), as shown in Fig. 2. The experiments were conducted in CO2-saturated 0.5 M KHCO3 and in Ar-saturated 0.5 M Na2SO4 electrolytes under continuous bubbling of the respective gas. The samples were pre-scanned at 10 mV/s for 5 cycles to ensure they reached equilibrium and stabilized before recording their actual response. Figure S1 reveals a broad peak for all the four samples under Ar bubbling in the potential range of − 0.6 to − 0.4 V vs. RHE, which can be attributed to the reduction of Cu2O53. The curve of sample 4-CuZn, however, shows a different peak between − 1 and − 0.8 V vs. RHE, which is likely ascribed to the reduction of ZnO53. Table S2 shows the extracted data from the LSV curves for each sample. It is also worth noting that at 0 V vs. RHE, the electrocatalysts showed non-zero current, likely because of double-layer charging and parasitic reactions at the surface of the electrode. It is difficult to eliminate these effects as LSV cannot distinguish between electrocatalyst, electrolyte, and charge transfer events54.

Linear scan voltammetry under continuous CO2 and Ar purge in 0.5 M KHCO3 and 0.5 M Na2SO4, respectively for samples (a) 1-CuZn, (b) 2-CuZn, (c) 3-CuZn, and (d) 4-CuZn.

The onset potential for the samples tested under CO2 shifts towards more negative potentials as the Zn content increases (from − 0.17 to − 0.851 V vs. RHE). This is likely due to the ability of Zn to suppress the hydrogen evolution reaction (HER), which is observed in Fig. 3a as well, where the FE of H2 is much less for the samples with high Zn content as compared to the samples with lower Zn content55,56. Not to mention that the difference in the current density generated between the curves under CO2 bubbling and Ar bubbling progressively becomes more pronounced as the Zn content increases. This is strong indication that most of the current density generated by sample 1-CuZn in the LSV is due to HER where the difference between the CO2 condition and Ar is least. Nevertheless, the onset potential is only a guiding parameter that should not be over-interpreted because it can be influenced by parasitic reactions and system sensitivity57. All in all, the addition of Zn to Cu, despite increasing the onset potential, minimizes the production of HER.

The electrocatalytic performance of the samples at a potential of − 0.91 V vs. RHE. (a) The measured Faradic efficiencies and (b) the chronoamperometry profiles with an inset of a photograph of the 4 polished brass samples.

The surface roughness (Table S3) coincides quite well with the obtained current density for each sample. Sample 1-CuZn has the highest roughness of 134.5 and, as a result, demonstrates one of the highest total current densities of 30 mA/cm2 at − 0.91 V vs. RHE. However, most of this current is consumed by the HER, which is a high competitor with CO2RR (Supplementary information Fig. S3). It is worth mentioning that surface roughness often influences the performance of the catalyst beyond just the value of the current density, namely the product selectivity. Hence, the early development of current observed in the LSV is most likely attributed to HER overwhelming the surface rather than CO2RR15,58,59. In our case, changing the Zn content is not only influencing the chemical nature of the catalyst but also the physical nature, i.e., the electrochemical active surface area (EASA)60,61. CO2RR relies on complicated mass transport equilibria within the buffer electrolyte and, as such, faces many kinetic barriers62,63.

Figure S3 shows the calculated FE of each of the samples over the measured potential range, which reveals a weak dependency between the FE and applied potential. Figure 3a shows the FEs at − 0.91 V vs. RHE. Samples 3-CuZn and 4-CuZn show the highest CO FE, reaching 30.8% and 30.6%, respectively, which means both samples share similar product selectivity. The difference of product selectivity between samples 3-CuZn and 4-CuZn is insignificant and the progression of Zn content with respect product FE leads to a plateau rather than a volcano shape. This suggests a saturation of activity with the addition of Zn beyond 30%. As for the reaction rate, sample 3-CuZn has the larger total current density yielding an average of 10.16 mA/cm2 at − 0.91 V vs. RHE throughout the 3600 s compared to 3.66 mA/cm2 for the 4-CuZn sample as shown in Fig. 3b. The decreased rate activity of 4-CuZn compared to 3-CuZn has been further investigated using density functional theory (DFT) simulations as discussed in a subsequent section.

It is well-established in the literature that Zn-based electrocatalysts tend to produce HCOO− as a liquid product, which is also observed with our brass electrocatalysts upon HPLC analysis of the electrolyte26,64,65. The results in Fig. 3a show that the sample with the least Zn content (1-CuZn) produced the least FE for HCOO− at 9.68%, while the sample with the highest Zn content (4-CuZn) produced the highest FE at 22.6%. Note that CO production likely takes place on the ZnO sites, while HCOO− production takes place on the reduced ZnO sites66,67. As a − 1.10 V vs. RHE potential (i.e., the reduction potential of Zn(II) at this particular pH) is applied, ZnO would always be reduced during the CO2RR experiment. In our case, CO2RR begins at − 1.16 V vs. RHE, which makes the production of HCOO− nearly unavoidable. This is further revealed from the XRD patterns in Fig. 4c of the samples after electrolysis, revealing the almost complete disappearance of the ZnO peaks, especially for samples 3-CuZn and 4-CuZn. This makes the selectivity control with respect to Zn very difficult and urges more designs to overcome such a challenge. The Cu2O and CuO have also disappeared due to the applied reduction bias. The state of the Cu however is likely a partially reduced phase between Cu2O and Cu metal as previously reported in the literature54.

(a) The partial current densities of CO across different Ag deposition times at − 0.91 V vs. RHE for sample 3-CuZn (b) Faradic efficiency and the ratio of product gases of 3-CuZn with different Ag depositions times at − 0.91 V vs. RHE (c) Grazing angle XRD patterns for all samples after electrochemical CO2RR at − 0.91 V vs. RHE (d) stability showing the current density and partial current density for 3-CuZn with 20 s Ag deposition at − 0.91 V vs. RHE.

To improve the selectivity, Ag was deposited on the surface of the brass samples with the assumption that Ag would stabilize the oxide species where its reduction would be minimized as well as introduce more active sites for CO production. Upon Ag deposition, sample 3-CuZn showed the best FE for CO production. The successful deposition of Ag was confirmed by the new Ag diffraction peaks that appeared at 39.56° (111), 45.74° (200), and 66.11° (220), as depicted in Fig. 5c. A new diffraction peak emerged at 44.34°, which is characteristic of AgZn, revealing the strong affinity of Ag towards Zn that is expected to impact the chemical nature of the overall electrocatalyst during the CO2RR68. Indeed, the results depicted in Fig. 4b, show the decrease in the formation of HCOO− from 21.6 to 7.53% after 5 s, and to 4.68% after 20 s until it becomes undetectable by the HPLC after 60 s. The XRD pattern (10) in Fig. 2c also shows the preservation of the ZnO peaks after CO2RR. Furthermore, Fig. S4a,b shows the SEM images of sample 3-CuZn after Ag deposition as indicated by the emerged rhombic features. Note that those features are retained after the CO2RR, revealing the role played by Ag in stabilizing ZnO, whereby it is able to withstand the reduction potentials of CO2RR. Ag can also promote CO production by introducing more active sites, as revealed in Fig. 4a. As the Ag deposition time increases, the partial current density, which can be approximated to the rate of CO production, also increases until reaching a maximum of 3.44 mA/cm2 in the time interval of 20–30 s. Thus, the addition of Ag improved the selectivity of 3-CuZn towards CO production. To complete the picture for the Ag deposited on brass, a stability measurement was performed as shown in Fig. 4d. The measurement was performed for 6 h, where the electrocatalyst maintained good stability throughout the test.

(a) Potential energy profile of the mechanism for the three proposed pathways for CO formation on sample 3-CuZn: direct dissociation, H-assisted via COOH*, and via HCOO*. (b) The projected density of states (PDOS) of the Cu atom in the four samples on the (111) plane and the d-band center represented by the black arrow while the Fermi level is the dotted line, and (c) the binding energy of the different adsorbates during CO2RR on the Ag–CuZn (111) surface, the red dot is the binding energy of CO.

As previously discussed, annealing the scrap brass samples in the air tends to form electrocatalysts that favor the formation of CO and CHOO−. In this regard, DFT calculations were performed to gain insights into the mechanism of the reaction as well as to explain the difference in activities between the samples69. CuZn (111) surface was studied in particular because it consistently showed the strongest peaks in the XRD spectra of the annealed samples (Fig. 1c). The sequence of CO2RR on the brass surface proceeds as depicted in Fig. 5a. Upon CO2 adsorption, Mulliken's charge analysis reveals the charge transfer from 3-CuZn (111) surface to the CO2 molecule. As a result, the CO2 molecule gains a negative charge of 0.52 e and forms a negatively charged CO2 anion. This leads to strong adsorption on the catalyst surface. As the reaction continues, the two C–O bond lengths are elongated, and the (O–C–O) angle is decreased from 180° to 135.9°, revealing the activation of CO2. To unveil the mechanism of the dissociation of CO2 on the 3-CuZn (111) surface, the following three possible routes for dissociation were elucidated: the direct dissociation and the H-assisted dissociation (the hydrogen source is the electrolyte in this case)70,71. Figure 5a shows the direct dissociation route, where the interaction between the 3-CuZn (111) surface and CO2 spontaneously forms CuZn-CO2* that is then dissociated to CuZn-CO* + O* via the transition state (TS1). This process is exothermic by − 0.04 eV and has an activation barrier of 1.48 eV. After that, absorption of 0.8 eV from ambient heat leads to the desorption of CO* from the surface to form CO gas. The second possible dissociation route is the H binding. In the presence of hydrogen, CO2 may be activated towards the formation of COOH* or HCOO*. In the case of carboxyl formation, hydrogen atom attacks one of the oxygen atoms of the CO2 and forms O–H bond, as depicted in Fig. 5a. This step passes through a transition state (TS2) of 1.49 eV. This step is endothermic by 0.32 eV followed by breaking of the C–O bond and forming adsorbed CO* and OH* via (TS3) of 0.55 eV. This process is exothermic by 0.47 eV. Concerning the formation of formate route, hydrogen atom binds to the carbon atom of CO2 through a transition state (TS4) of 1.03 eV, which is an exothermic process of 0.64 eV. Then it splits into HCO* and O* followed by hydrogen transfer to the O* to form CO* and OH* through a barrier of 0.55 eV. The adsorbed CO* desorbs in the gaseous form by 0.93 eV. Although both pathways are viable, our results reveal that the direct dissociation is more thermodynamically favorable. It is also important to note that this particular catalyst surface does not promote C–C coupling, which also would explain the lack of C2+ products in the experimental tests. The three mechanisms are shown in more detail in supplementary information Figs. S10–S14.

In order to better understand the selectivity and activity of the electrocatalysts, calculations of the electronic states for all the four different samples (1-CuZn, 2-CuZn, 3-CuZn, 4-CuZn) and Ag-coated 3-CuZn were carried out. Figure 5b shows the projected density of states (PDOS) for Cu atom in each system and its d-band center (εd). The position of the d-band center with respect to the Fermi level is important because it indicates the availability of electrons in the atom72. Thus, εd is strongly correlated to the binding energy, and it is often used as a metric for catalytic activity73. A εd that is closer to the Fermi level pushes the antibonding states above the Fermi level where they will be less filled and hence stronger binding between the catalyst and the absorbed intermediates74,75. The four samples along with the Ag deposited sample show relatively close εd values as seen in Fig. 5b. The largest difference in the samples’ d-band is 0.69 eV between 3-AgCuZn and 1-CuZn which suggests that the electronic effect on the performance of the electrocatalysts might not have profound overall impact42,76. The more dominate parameter is perhaps the geometric differences between each of the catalysts’ nanostructures as discussed in characterization analysis. This coincides with the experimental findings in a very specific way; the addition of Ag to the best performing sample, 3-CuZn, did not impact the FE towards CO significantly but rather impacted the partial current density for CO. This enhanced activity for CO specifically is likely owed to the structural changes induced by the Ag rather than the chemical.

As for the selectivity (i.e. the chemical nature) towards CO production specifically, Fig. 5c depicts the binding strength of the different adsorbates that are likely to form during the CO2RR process on the most energetically favorable site on the 3-AgCuZn surface. The CO molecule, which is represented by the red dot, has the least binding energy among all the other possible products especially the products that are rank higher in electron transfers. This suggest that its desorption of CO after its formation is the more likely event rather than its further reaction. This is indeed what is observed experimentally as the formation of formate is decreased substantially while the formation of CO is enhanced.

A simple, inexpensive, and scalable method to repurpose scrap brass metal alloys for CO2RR to produce syngas at a reasonable rate was demonstrated. Scraped brass samples with different Zn content were activated via annealing in an air atmosphere, where various nanostructures emerged. Increasing the Zn content led to the formation of denser nanoneedles. As revealed via the XRD analysis, the formation of ZnO was found to inhibit the HER and promote the formation of both CO and CHOO. The Faradic efficiency (FE) of the samples showed weak dependency on voltage. This should be beneficial from an industrial perspective as it is hard to control the working electrode potential in real electrolyzers, where no reference electrodes are being used. The 3-CuZn electrocatalyst with 30% Zn was found to be the best performing among all tested samples with FEs of 30.7% and 21.6% for CO and CHOO−, respectively. The addition of Ag improved the performance of the electrocatalyst by increasing the partial current density towards the formation of CO. The DFT calculations confirmed the obtained experimental results in terms of possible formed intermediates and calculated d-band center (εd). The brass alloy modified by Ag showed the lowest binding energy for CO indicating its facile release and preferred production over any other product.

Wei, T. et al. Developed and developing world responsibilities for historical climate change and CO2 mitigation. Proc. Natl. Acad. Sci. U.S.A. 109, 12911–12915 (2012).

Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

Davis, S. J., Caldeira, K. & Matthews, H. D. Future CO2 emissions and climate change from existing energy infrastructure. Science 329, 1330–1333 (2010).

Article  ADS  CAS  PubMed  Google Scholar 

Matinde, E., Simate, G. S. & Ndlovu, S. Mining and metallurgical wastes: A review of recycling and re-use practices. J. South Afr. Inst. Min. Metall. 118, 825–844 (2018).

Zhang, L. & Xu, Z. A critical review of material flow, recycling technologies, challenges and future strategy for scattered metals from minerals to wastes. J. Clean. Prod. 202, 1001–1025 (2018).

Hasan, M. M. et al. Intermolecular electron transfer in electrochemically exfoliated BCN-Cu nanosheet electrocatalysts for efficient hydrogen evolution. ACS Appl. Energy Mater. https://doi.org/10.1021/acsaem.2c01349 (2022).

Gomaa, A. K. et al. Facile surface treatment of industrial stainless steel waste meshes at mild conditions to produce efficient oxygen evolution catalysts. Energy & Fuels 36, 7025–7034 (2022).

Hertwich, E., Lifset, R., Pauliuk, S. & Heeren, N. Resource Efficiency and Climate Change: Material Efficiency Strategies for a Low-Carbon Future (United Nations Environment Programme, 2020).

Salem, K. E. et al. Unveiling the optimal interfacial synergy of plasma modulated trimetallic Mn‐Ni‐Co phosphides: Tailoring deposition ratio for complementary water splitting.  Energy Environ. Mater. https://doi.org/10.1002/eem2.12324 (2022).

Sassenburg, M. Conducting CO2 reduction at a bipolar membrane electrode assembly (2018).

Ma, Z. et al. Enhanced electrochemical CO2 reduction of Cu@CuxO nanoparticles decorated on 3D vertical graphene with intrinsic sp3-type defect. Adv. Funct. Mater. 30, 1–12 (2020).

Zhang, R. Z. et al. Design strategies and mechanism studies of CO2 electroreduction catalysts based on coordination chemistry. Coord. Chem. Rev. 422, 1–28 (2020).

Stolar, T. et al. Scalable mechanochemical amorphization of bimetallic Cu–Zn MOF-74 catalyst for selective CO2 reduction reaction to methanol. ACS Appl. Mater. Interfaces 13, 3070–3077 (2021).

Article  CAS  PubMed  Google Scholar 

Li, X. et al. Selective electroreduction of CO2 and CO to C2H4 by synergistically tuning nanocavities and the surface charge of copper oxide. ACS Sustain. Chem. Eng. https://doi.org/10.1021/acssuschemeng.2c01600 (2022).

Hao, L. & Sun, Z. Metal oxide-based materials for electrochemical CO2 reduction. Wuli Huaxue Xuebao Acta Phys. Chim. Sin. 37, 1–19 (2021).

Kuhl, K. P., Cave, E. R., Abram, D. N. & Jaramillo, T. F. New insights into the electrochemical reduction of carbon dioxide on metallic copper surfaces. Energy Environ. Sci. 5, 7050–7059 (2012).

Tomboc, G. M., Choi, S., Kwon, T., Hwang, Y. J. & Lee, K. Potential link between Cu surface and selective CO2 electroreduction: Perspective on future electrocatalyst designs. Adv. Mater. 32, 1908398 (2020).

Ghosh, S., Garapati, M. S., Ghosh, A. & Sundara, R. Nonprecious catalyst for three-phase contact in a proton exchange membrane CO2 conversion full cell for efficient electrochemical reduction of carbon dioxide. ACS Appl. Mater. Interfaces 11, 40432–40442 (2019).

Article  CAS  PubMed  Google Scholar 

Li, X., Hong, S., Hao, L. & Sun, Z. Cadmium-based metal–organic frameworks for high-performance electrochemical CO2 reduction to CO over wide potential range. Chin. J. Chem. Eng. 43, 143–151 (2022).

Fan, Q. et al. Activation of Ni particles into single Ni–N atoms for efficient electrochemical reduction of CO2. Adv. Energy Mater. 10, 1–8 (2020).

Bondue, C. J., Graf, M., Goyal, A. & Koper, M. T. M. Suppression of hydrogen evolution in acidic electrolytes by electrochemical CO2 reduction. J. Am. Chem. Soc. 143, 279–285 (2021).

Article  CAS  PubMed  Google Scholar 

Ismail, A. M., Samu, G. F., Balog, Á., Csapó, E. & Janáky, C. Composition-dependent electrocatalytic behavior of Au-Sn bimetallic nanoparticles in carbon dioxide reduction. ACS Energy Lett. 4, 48–53 (2019).

Mahyoub, S. A. et al. Rational design of low loading Pd-alloyed Ag nanocorals for high current density CO2-to-CO electroreduction at elevated pressure. Mater. Today Energy 24, 100923 (2022).

Dongare, S., Singh, N. & Bhunia, H. Oxide-derived Cu–Zn nanoparticles supported on N-doped graphene for electrochemical reduction of CO2 to ethanol. Appl. Surf. Sci. 556, 149790 (2021).

Dongare, S., Singh, N., Bhunia, H. & Bajpai, P. K. Electrochemical reduction of CO2 using oxide based Cu and Zn bimetallic catalyst. Electrochim. Acta 392, 138988 (2021).

Keerthiga, G. & Chetty, R. Electrochemical reduction of carbon dioxide on zinc-modified copper electrodes. J. Electrochem. Soc. 164, H164–H169 (2017).

Yin, G. et al. Selective electro- or photo-reduction of carbon dioxide to formic acid using a Cu–Zn alloy catalyst. J. Mater. Chem. A 5, 12113–12119 (2017).

Feaster, J. T. et al. Understanding selectivity for the electrochemical reduction of carbon dioxide to formic acid and carbon monoxide on metal electrodes. ACS Catal. 7, 4822–4827 (2017).

He, J., Dettelbach, K. E., Huang, A. & Berlinguette, C. P. Brass and bronze as effective CO2 reduction electrocatalysts. Angew. Chem. 129, 16806–16809 (2017).

Jeon, H. S. et al. Operando insight into the correlation between the structure and composition of CuZn nanoparticles and their selectivity for the electrochemical CO2 reduction. J. Am. Chem. Soc. 141, 19879–19887 (2019).

Article  CAS  PubMed  PubMed Central  Google Scholar 

Lv, J. J. et al. A highly porous copper electrocatalyst for carbon dioxide reduction. Adv. Mater. 30, 1–8 (2018).

Chang, Y. C., Lin, P. S., Liu, F. K., Guo, J. Y. & Chen, C. M. One-step and single source synthesis of Cu-doped ZnO nanowires on flexible brass foil for highly efficient field emission and photocatalytic applications. J. Alloys Compd. 688, 242–251 (2016).

Zhong, H. et al. Synergistic electroreduction of carbon dioxide to carbon monoxide on bimetallic layered conjugated metal-organic frameworks. Nat. Commun. 11, 1–10 (2020).

Hjorth, I., Nord, M., Rønning, M., Yang, J. & Chen, D. Electrochemical reduction of CO2 to synthesis gas on CNT supported CuxZn1−xO catalysts. Catal. Today 357, 311–321 (2020).

Miftahurrahman, G., Setiarahayu, H. & Nandiyanto, A. B. D. An economic evaluation on scaling-up production of nano gold from laboratory to industrial scale. Indones. J. Comput. Eng. Des. 1, 29 (2019).

Tsuzuki, T. Commercial scale production of inorganic nanoparticles. Int. J. Nanotechnol. 6, 567–578 (2009).

Article  ADS  CAS  Google Scholar 

Stojkovikj, S. et al. Electrocatalyst derived from waste Cu–Sn bronze for CO2 conversion into CO. ACS Appl. Mater. Interfaces. https://doi.org/10.1021/acsami.1c05015 (2021).

Dutta, A., Rahaman, M., Luedi, N. C., Mohos, M. & Broekmann, P. Morphology matters: Tuning the product distribution of CO2 electroreduction on oxide-derived cu foam catalysts. ACS Catal. 6, 3804–3814 (2016).

Li, D. et al. Tuning the pore structure of porous tin foam electrodes for enhanced electrochemical reduction of carbon dioxide to formate. Chem. Eng. J. 375, 122024 (2019).

Hu, H. et al. In-situ grown nanoporous Zn–Cu catalysts on brass foils for enhanced electrochemical reduction of carbon dioxide. Appl. Surf. Sci. 445, 281–286 (2018).

Article  ADS  CAS  Google Scholar 

Segall, P. J. D. et al. First-principles simulation: Ideas, illustrations and the CASTEP code. J. Phys. Condens. Matter 14, 2717–2744 (2002).

Article  ADS  CAS  Google Scholar 

Peterson, A. A., Abild-Pedersen, F., Studt, F., Rossmeisl, J. & Nørskov, J. K. How copper catalyzes the electroreduction of carbon dioxide into hydrocarbon fuels. Energy Environ. Sci. 3, 1311–1315 (2010).

Ma, M. et al. Electrochemical reduction of CO2 on compositionally variant Au–Pt bimetallic thin films. Nano Energy 42, 51–57 (2017).

Article  ADS  CAS  Google Scholar 

Dattila, F., Garclá-Muelas, R. & López, N. Active and selective ensembles in oxide-derived copper catalysts for CO2 reduction. ACS Energy Lett. 5, 3176–3184 (2020).

Eissa, D.S., El-Hagar, S.S., Ashour, E.A. & Allam, N.K. Electrochemical nano-patterning of brass for stable and visible light-induced photoelectrochemical water splitting. Int. J. Hydrogen Energy 44, 14588–14595 (2019).

Pander, J. E. et al. Understanding the heterogeneous electrocatalytic reduction of carbon dioxide on oxide-derived catalysts. ChemElectroChem 5, 219–237 (2018).

Varandili, S. B. et al. Elucidating the structure-dependent selectivity of CuZn towards methane and ethanol in CO2 electroreduction using tailored Cu/ZnO precatalysts. Chem. Sci. 12, 14484–14493 (2021).

Article  CAS  PubMed  PubMed Central  Google Scholar 

Zoolfakar, A. S., Rani, R. A., Morfa, A. J., O’Mullane, A. P. & Kalantar-Zadeh, K. Nanostructured copper oxide semiconductors: A perspective on materials, synthesis methods and applications. J. Mater. Chem. C 2, 5247–5270 (2014).

Li, Y. B., Bando, Y. & Golberg, D. ZnO nanoneedles with tip surface perturbations: Excellent field emitters. Appl. Phys. Lett. 84, 3603–3605 (2004).

Article  ADS  CAS  Google Scholar 

Li, X. & Wang, Y. Structure and photoluminescence properties of Ag-coated ZnO nano-needles. J. Alloys Compd. 509, 5765–5768 (2011).

Allam, N.K., Nazeer, A. A., Youssef, G. I. & Ashour, E. A. Electrochemical and stress corrosion cracking behavior of α-aluminum bronze and α-brass in nitrite solutions: a comparative study. Corrosion 69, 77–84 (2013).

Ungár, T. Microstructural parameters from X-ray diffraction peak broadening. Scr. Mater. 51, 777–781 (2004).

Bindu, P. & Thomas, S. Estimation of lattice strain in ZnO nanoparticles: X-ray peak profile analysis. J. Theor. Appl. Phys. 8, 123–134 (2014).

Kabasakaloǧlu, M., Kiyak, T., Şendil, O. & Asan, A. Electrochemical behavior of brass in 0.1 M NaCl. Appl. Surf. Sci. 193, 167–174 (2002).

Anantharaj, S., Noda, S., Driess, M. & Menezes, P. W. The pitfalls of using potentiodynamic polarization curves for Tafel analysis in electrocatalytic water splitting. ACS Energy Lett. 6, 1607–1611 (2021).

Bayaguud, A., Fu, Y. & Zhu, C. Interfacial parasitic reactions of zinc anodes in zinc ion batteries: Underestimated corrosion and hydrogen evolution reactions and their suppression strategies. J. Energy Chem. 64, 246–262 (2022).

Nguyen, D. L. T. et al. Effect of halides on nanoporous Zn-based catalysts for highly efficient electroreduction of CO2 to CO. Catal. Commun. 114, 109–113 (2018).

Botz, A. J. R., Nebel, M., Rincón, R. A., Ventosa, E. & Schuhmann, W. Onset potential determination at gas-evolving catalysts by means of constant-distance mode positioning of nanoelectrodes. Electrochim. Acta 179, 38–44 (2015).

Jiang, K. et al. Effects of surface roughness on the electrochemical reduction of CO2 over Cu. ACS Energy Lett. 5, 1206–1214 (2020).

Tang, W. et al. The importance of surface morphology in controlling the selectivity of polycrystalline copper for CO2 electroreduction. Phys. Chem. Chem. Phys. 14, 76–81 (2012).

Article  CAS  PubMed  Google Scholar 

Ajmal, S. et al. Zinc-modified copper catalyst for efficient (photo-)electrochemical CO2 reduction with high selectivity of HCOOH production. J. Phys. Chem. C 123, 11555–11563 (2019).

Feng, Y. et al. Laser-prepared CuZn alloy catalyst for selective electrochemical reduction of CO2 to ethylene. Langmuir 34, 13544–13549 (2018).

Article  CAS  PubMed  Google Scholar 

Goyal, A., Marcandalli, G., Mints, V. A. & Koper, M. T. M. Competition between CO2 reduction and hydrogen evolution on a gold electrode under well-defined mass transport conditions. J. Am. Chem. Soc. 142, 4154–4161 (2020).

Article  CAS  PubMed  PubMed Central  Google Scholar 

Dunwell, M. et al. Examination of near-electrode concentration gradients and kinetic impacts on the electrochemical reduction of CO2 using surface-enhanced infrared spectroscopy. ACS Catal. 8, 3999–4008 (2018).

Zeng, J. et al. Coupled copper–zinc catalysts for electrochemical reduction of carbon dioxide. Chemsuschem 13, 4128–4139 (2020).

Article  CAS  PubMed  Google Scholar 

Mohamed, A. G. A. et al. Asymmetric oxo-bridged ZnPb bimetallic electrocatalysis boosting CO2-to-HCOOH reduction. Adv. Sci. 2104138, 1–10 (2021).

Chen, T. L. et al. In situ unraveling of the effect of the dynamic chemical state on selective CO2 reduction upon zinc electrocatalysts. Nanoscale 12, 18013–18021 (2020).

Article  CAS  PubMed  Google Scholar 

Daiyan, R. et al. Uncovering atomic-scale stability and reactivity in engineered zinc oxide electrocatalysts for controllable syngas production. Adv. Energy Mater. 10, 1–9 (2020).

Lu, Q. et al. Uniform Zn deposition achieved by Ag coating for improved aqueous zinc-ion batteries. ACS Appl. Mater. Interfaces 13, 16869–16875 (2021).

Article  CAS  PubMed  Google Scholar 

Nunomura, N. Density functional theory study of Cu–Zn alloys. 902012035, 7–10 (2012).

Nitopi, S. et al. Progress and perspectives of electrochemical CO2 reduction on copper in aqueous electrolyte. Chem. Rev. https://doi.org/10.1021/acs.chemrev.8b00705 (2019).

Liu, L. & Lv, P. DFT insight into the effect of Cu atoms on adsorption and dissociation of CO2 over a Pd8/TiO2(101) surface. RSC Adv. 11, 17391–17398 (2021).

Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

Jiao, S., Fu, X. & Huang, H. Descriptors for the evaluation of electrocatalytic reactions: d-band theory and beyond. Adv. Funct. Mater. 32, 1–43 (2022).

Zhang, Z. et al. ‘Two ships in a bottle’ design for Zn–Ag–O catalyst enabling selective and long-lasting CO2 electroreduction. J. Am. Chem. Soc. 143, 6855–6864 (2021).

Article  CAS  PubMed  Google Scholar 

Xiao, J. & Frauenheim, T. Theoretical insights into CO2 activation and reduction on the Ag(111) monolayer supported on a ZnO(0001) substrate. J. Phys. Chem. C 117, 1804–1808 (2013).

Nørskov, J. K., Bligaard, T., Rossmeisl, J. & Christensen, C. H. Towards the computational design of solid catalysts. Nat. Chem. 1, 37–46 (2009).

Article  PubMed  CAS  Google Scholar 

Xiao, J. & Frauenheim, T. Theoretical insights into CO2 activation and reduction on the Ag(111) monolayer supported on a ZnO(000 1) substrate. J. Phys. Chem. C 117, 1804–1808 (2013).

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This study was funded by the Climate Change Funding from AUC (No. CCI-SSE-PHYS-08).

Energy Materials Laboratory (EML), School of Sciences and Engineering, The American University in Cairo, New Cairo, 11835, Egypt

Ibrahim M. Badawy, Ahmed Mohsen Ismail, Ghada E. Khedr, Manar M. Taha & Nageh K. Allam

Department of Analysis and Evaluation, Egyptian Petroleum Research Institute, Cairo, 11727, Egypt

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

I.M.B. carried out the experimental work and wrote the manuscript with support from A.M.I. G.E.K. carried out the DFT calculations and wrote the corresponding section, while M.M.T. was responsible for the HPLC measurements. N.K.A. analyzed the results, wrote the manuscript, secured the funding, and supervised the work. All authors have given approval to the final version of the manuscript.

Correspondence to Nageh K. Allam.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Badawy, I.M., Ismail, A.M., Khedr, G.E. et al. Selective electrochemical reduction of CO2 on compositionally variant bimetallic Cu–Zn electrocatalysts derived from scrap brass alloys. Sci Rep 12, 13456 (2022). https://doi.org/10.1038/s41598-022-17317-6

DOI: https://doi.org/10.1038/s41598-022-17317-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Scientific Reports (Sci Rep) ISSN 2045-2322 (online)

Selective electrochemical reduction of CO2 on compositionally variant bimetallic Cu–Zn electrocatalysts derived from scrap brass alloys | Scientific Reports